Expandable biodegradable polymeric stents for combined mechanical support and pharmacological or radiation therapy

ABSTRACT

An expandable biodegradable polymeric stent is fabricated with biodegradable polymer fibers (Poly-L-lactic acid, PLLA) in a coil shape that is constructed with both central and external or internal peripheral lobes. It is delivered and expanded using a conventional angioplasty balloon system. The disclosed stent can serve as a temporary scaffold for coronary vessels after PTCA or for peripheral endovascular stenting, or it can provide mechanical palliation for strictures of ductile organs (trachea, esophagus, bile and pancreatic ducts, ureter etc.). The disclosed stent also serves as a unique device for specific local drug delivery. Therapeutic agents (chemical compounds, protein enzyme and DNA sequences) and cells can be loaded into the stent and gradually released to target tissues. Local radiation therapy can also be delivered by a specially adapted stent.

TECHNICAL FIELD OF THE INVENTION

This invention generallyrelates to stents for implantation into blood vessels or other organs, and more specifically to stents that are absorbable over time and capable of local drug/gene delivery for enhancing therapeutic effects.

BACKGROUND OF THE INVENTION

Intraluminal stents are commonly employed for treatment of various vascular conditions such as arteriosclerosis, often as coronary artery implants. A stent can be implanted at the site of a vessel stricture or stenosis using a conventional balloon catheter delivery system as used in angioplasty. Stents also maybe employed in bodypassageways other than blood vessels to treat strictures or prevent luminal occlusion. Such stents ordinarily consist of a cylindrical network of very small metal wires. The stent is inserted in a small-diameter configuration and then expanded to a large-diameter final configuration against the walls of the blood vessel or other body lumen. Such stent structures and implantation techniques are well known.

Great efforts have been expended to modify metallic stents to eliminate stress-induced and/or inflammation-induced restenosis, and to effectively deliver therapeutic agents to lesion sites. Some advancements in drug-coated metal stents have been made recently. However, metallic stents still present a potential vessel injury problem. Furthermore, the delivery of medicine to a lesion site either by local or systemic means is unsatisfactory with current stent and catheter technology. The present invention addresses these problems.

SUMMARY OF THE INVENTION

In accordance with a principal object of the present invention, luminal support and localized treatment of lesion sites within body passageways is accomplished by the implantation of an expandable biodegradable polymeric stent that includes therapeutic agents. By virtue of its gradual absorption over time, the inventive stent avoids residual stress, and permits local drug delivery or local radiation treatment.

In its preferred implantation, the stent of the present invention provides adequate mechanical support during and following the interventional procedure, and, by being absorbed over controllable periods, avoids chronic mechanical disturbance of the vessel wall. The residual stress against the vessel wall is eliminated after the stent is degraded. During the degradation process, loaded therapeutic agents are released in a controlled fashion, and effective concentrations at target lesions can be maintained. Local radiation treatment can likewise be maintained.

The stent of the present invention preferably has the following features: (1) it has an all-polymer construction with similar mechanical function to conventional metallic stents; (2) it is constructed with fiber cords having both central and peripheral lobes and is stabilized by longitudinal rods, thus presenting a low profile during delivery and a large effective diameter following expansion; (3) it is expandable with an expansion ratio that can be customized to meet various needs; (4) it can be deployed at body temperature with low inflation pressure (3 atm); (5) it is a temporary implant; (6) it may be a local drug or gene delivery device; (7 ) it may be a local radiation therapy device; and (8) it can include fibers with various functions (mechanical support, acute drug burst, long-term drug release, etc.), enabling a variety of treatment options including multiple functions with a single stent and using a single stent-implant procedure.

The present invention has a number of advantages over conventional stents. Firstly, in contrast to metal stents, the polymeric stent of the present invention is a temporary implant. The temporary residence permits the residual stress against the vessel wall to be resolved, a factor commonly leading to in-stent restenosis in the case of metallic stents. Secondly, the inventive stent is also capable of carrying therapeutic agents either incorporated in the polymer bulk or coated on the polymer surface. Thirdly, it is possible to control the operation of the inventive stent by selection of the polymer composition, the polymer molecular weight, fiber cord diameter and processing conditions, thus controlling the degradation rate, drug release rate and period of mechanical support. Fourthly, compared with tubular-shaped polymeric stents, the inventive stent has superior expandability and flexibility. Additionally, the inventive stent also has advantages over the “zigzag” polymeric stent recently disclosed in the prior art (Circulation, vol. 102, pp. 399-404, 2000), since it is deployed at body temperature with low inflation pressure.

In addition to being biodegradable, the stent of the present invention synergistically combines excellent mechanical support and local drug delivery, for both short-term and long-term applications. Current metallic stents are incapable of delivering drugs without polymer coatings. Moreover, metallic stents are known to be a stimulus for chronic vessel injury. Other current approaches, such as the combination of a metallic stent and bolus drug delivery by a porous angioplasty balloon, provide both mechanical support and short-term drug delivery. However, other than initial control of drug concentration at the lesion site, the porous angioplasty balloon approach is limited in its application and is incapable of performing certain desirable functions, such as prolonged drug delivery and transient radiation therapy. The biodegradable polymeric stent of the present invention provides sufficient mechanical strength as well as controllable short-term and long-term drug delivery while eliminating the stimulus for chronic vessel wall injury.

BRIEF DESCRIPTION OF THE DRAWINGS

For a more complete understanding of the present invention and the advantages thereof reference is now made to the following description taken in conjunction with the accompanying Drawings in which:

FIG. 1 is a schematic illustration of the three-dimensional structure of an expandable stent according to the present invention;

FIGS. 2A, 2B and 2C are schematic end views of the inventive stent at three stages during deployment with an inflatable balloon shown therein in phantom, FIG. 2A showing the stent in its furled state, FIG. 2B showing the stent in a partially expanded state, and FIG. 2C showing the stent in its fully expanded state;

FIG. 2D is a schematic perspective view of the inventive stent in its fully expanded state; and

FIGS. 3A and 3B are schematic end views of an alternative embodiment of the inventive stent.

DETAILED DESCRIPTION OF THE INVENTION

Referring to FIG. 1, a preferred embodiment of a stent according to the present invention is shown and generally designated by reference numeral 10. The stent 10 comprises a coiled cord 50 of non-metallic material, preferably a polymer fiber or ply of multiple polymer fibers, wherein the polymer preferably comprises Poly-L-Lactic Acid (“PLLA”). The use of PLLA to construct the stent 10 is advantageous because it is biodegradable. It degrades away gradually within the body, the chemical products of the degradation process being primarily carbon dioxide and water, which are harmless to the host patient. Degradation occurs over a period of about six months to three years, mainly depending on the molecular weight of the polymer employed. PLLA is also advantageous because it can be impregnated with drugs or other chemical agents for local treatment of tissue at the stent implant site.

By way of example, the stent 10 of FIG. 1 is constructed with twelve coil rotations of a single-fiber cord, each rotation having one central lobe 20 and three peripheral lobes 30. The twelve central lobes 20 form the backbone of the stent 10. Three longitudinal rods 40 are attached on the exterior surface of the central lobes 20, preferably using a viscous PLLA-chloroform solution. The rods 40 may comprise the same single-fiber material as the coil of lobes 20 and 30. Alternatively, the coil of lobes 20 and 30 and the rods 40 may comprise a multiple-fiber ply material. For example, the coil of lobes 20 and 30 may be formed from a double-fiber ply material, and each of the three rods 40 maybe formed from a triple-fiber ply material for added rigidity. Also, by way of example, the length of inventive stent is 15 mm and the initial diameter is 1.9 mm. In this example, the final diameter, after balloon expansion, can reach 3.24 mm. The length of the stent can be increased by increasing the number of coil rotations. The peripheral and central lobe diameters determine the final diameter of the stent. To assure mechanical integrity, it is preferred that the coiled lobes 20 and 30 of the stent 10 be formed from a single cord that is continuous end-to-end.

The mechanical strength of the stent 10 can easily be varied (1) by adjusting the coil density; or (2) by adjusting the fiber ply. In practice, a stent with 15 coil rotations and a length of 15 mm will be stronger than a stent of the same length with 12 rotations. However, a stent in which the cord 50 is composed of a multiple-fiber ply will have higher resistance to radial compression. A double-fiber ply will have about twice the radial compression resistance of a single-fiber construction, and triple-fiber ply will have about three times the radial compression resistance of a single-fiber construction. Additionally, the diameter of the stent 10 can be adjusted (1) by adjusting the diameter of central and peripheral lobes; or (2) by adjusting the number of multiple peripheral lobes percentral lobe. The stent diameter increases as the diameter of central and peripheral lobes increases, and vise versa. It will also be appreciated that more peripheral lobes with the same diameter results in a stent of larger diameter in its fully expanded state.

The above-described design provides an excellent way to maximize the expandability of a polymeric stent. The major difference between metal and polymeric stent materials is that metal is more malleable and generally has a greater tensile strength. Thus, a metal wire can be deformed without affecting mechanical strength. In contrast, a polymer fiber cord cannot retain its original mechanical strength following permanent deformation (bending, for example). Despite the lower mechanical strength of polymeric materials relative to metals,- the polymeric stent of the present invention has sufficient strength to retain its shape in the expanded state, thereby stabilizing the vessel or duct wall for the intended purposes as with a conventional metal stent.

In accordance with an important concept of the invention, an extra length of cord is provided by the peripheral lobes to facilitate expansion from the furled state to the final large-diameter state. If the desired final length of the stent in the furled, multiple-lobe configuration is known, stents can be prepared using the exact same initial length of cord. After expansion, the final deployed length is achieved without damaging cord. It will be appreciated that this approach to stent design and fabrication provides a polymeric stent with excellent mechanical strength and flexibility for effective implantation.

According to another important feature of the invention, the longitudinal rods 40 provide support for the flexible coiled cord 50. Furthermore, the longitudinal rods 40 maintain the axial length of the stent 10 constant as its radial dimension increases during expansion. Solid wall tubular stents have the practical limitations that they are relatively inflexible, making it difficult for them to pass through sometimes tortuous vessel networks. This is because their relatively rigid cylindrical structure reduces the freedom to bend in all directions. In this invention, the integrity of the stent 10 is maintained by the longitudinal rods 40, three in embodiment of FIG. 1 preferably arranged at 120° intervals. Therefore, the expandable stent 10 has the inherent flexibility of a coil design yet has sufficient rigidity for effective handling due to the presence of the longitudinal rods 40. The advantages of this design compared with currently available clinical metal models will be readily apparent to the skilled practitioner.

It should be mentioned that the number of longitudinal reinforcing rods can be selected based on the number of peripheral lobes that design considerations dictate. Preferably, the longitudinally aligned groups of peripheral lobes are equal in number to the longitudinal reinforcing rods, which are alternately positioned so that each rod is midway between its two neighboring peripheral lobe groups. In FIG. 1, the preferred arrangement is illustrated in which there are three longitudinal reinforcing rods 40 and three longitudinally aligned groups of peripheral lobes 30.

Prototypes of the inventive stent have been constructed using a fixture and manually winding a fiber cord in a spiral fashion along the fixture. The fixture employed included a central cylindrical mandrel attached to a base at one end, and three cylindrical side posts attached to the base and extending along and parallel to the mandrel, the posts being circumferentially spaced around the mandrel at 120° intervals. The stent is constructed by attaching one end of the cord to the free end of the mandrel, then winding the cord around the mandrel, and successively looping the cord around the posts moving downward toward the base until twelve rotations of the mandrel have been completed. Periodically during the winding process, each of three longitudinal rods 40 are attached to the central lobes 20 in the manner depicted in FIG. 1. Upon completion, the stent is slidably removed from the mandrel and side posts. Design of an automated system is contemplated for reducing the labor-intensive winding process used to make the prototype stents.

The stent delivery and deployment system is based on conventional balloon catheter delivery systems used currently in clinical angioplasty. Therefore, the stent of the present invention can be implanted in practice using much of the conventional clinical deployment techniques used with metal stents.

FIGS. 2A-D illustrate the procedure of stent expansion and the structure of an expanded stent. In FIG. 2A, the stent 10 is in its small-diameter furled state, which enables the stent 10 to readily travel through a vessel to a site where it is to be deployed. A balloon 60, shown in phantom, is provided inside the stent 10 to effect expansion. In this end view, the symmetrical spacing of the three rods 40 with the three longitudinally aligned groups of peripheral lobes 30 can be envisioned more clearly when considered together with FIG. 1. In the small-diameter furled state, it will be seen that the central lobes 20 viewed from the end of the stent 10 are generally triangular in shape. Thus, the term “small-diameter” is used herein to describe the relative size of the stent 10 in the original furled state, the “diameter” in this context being the effective diameter of a circle or imaginary cylinder tangentially contacting the outer ends of the peripheral lobes 30.

In FIG. 2B, the stent 10 is starting to expand under the force of the expanding balloon 60, as indicated by the arrows. For comparison, dashed lines are provided in FIG. 2B to show the configuration of the stent 10 in its original furled state as depicted in FIG. 2A.

In FIG. 2C, the stent 10 is shown in its large-diameter, fully expanded state, in which the peripheral lobes 30 (shown in FIGS. 2A and 2B) have disappeared, their cord lengths having merged into the central lobe 20 of each of the twelve coils. Experimental data reveals that the stent 10 expands uniformly under increasing balloon pressure until it reaches its final diameter. The terms “final diameter” and “large-diameter” are used to describe the relative size of the stent 10 in its fully expanded state as depicted in FIG. 2C, the “diameter” being the effective diameter of a circle or imaginary cylinder tangentially contacting the outer edges of the longitudinal rods 40. FIG. 2C is not drawn to an accurate relative scale compared to FIG. 2A. In practice, it has been found that sufficient cord length can be provided in the peripheral lobes 30 to cause the effective diameter of the stent 10 to approximately double in size going from the original furled state of FIG. 2A to the final fully expanded state of FIG. 2C.

FIG. 2D shows the stent 10 with the balloon removed in its large-diameter state and also depicts the longitudinal rods 40 in their 1200 spaced peripheral positions along the length of the stent 10. The helical nature of the stent 10 in its fully expanded state is evident in FIG. 2D. Though the central lobes 20 are derived from a single cord of polymeric material that generally defines a helix in the fully expanded state, each lobe 20 can be viewed as one 360° length of cord with a leading end and a trailing end spaced apart by one-twelfth (in the case of a twelve-lobe stent) of the length of the stent 10. For example, to illustrate this concept, the first lobe 20 a at the right end of the stent 10 of FIG. 2D has a leading end 70 and a trailing end 80. The trailing end 80 of the first lobe 20 a corresponds to the leading end of the second lobe 20 b. The pattern continues through the length of the stent 10, each lobe's trailing end corresponding to the next successive lobe's leading end until the last lobe is reached, whose trailing end (not shown in FIG. 2D) is the free end of the cord 50 at the left end of the stent 10.

It will be appreciated from FIGS. 1 and 2A that the stent 10 in its original furled state has a more complex shape. From the example shown in FIG. 2A, it will be appreciated that each central lobe 20 has three peripheral lobes 30, a leading one of which being defined by a portion of the cord 50 that adjoins the leading end of the corresponding central lobe 20, a trailing one of which being defined by a portion of the cord 50 that adjoins the trailing end of the corresponding central lobe 20, and the last of the three peripheral lobes 30 being defined by a portion of the cord 50 at an intermediate point of the corresponding central lobe 20.

The stent 10 of the present invention can be adapted to a broad range of inflation pressures from 3 to 10 atm (a maximum pressure possibly even exceeding 10 atm). Experimental data has shown that, using a double-fiber ply stent, full expansion occurs at about 3 atm, and that the fully expanded diameter is stably maintained at inflation pressures of up to 10 atm. In the above-described example, the stent 10 has limited recoil about 4% when in an unstressed condition. The collapsing pressure holds at least up to 16 psi (i.e., greater than 1 atm), which is comparable to conventional metal stents.

It will be appreciated that the preferred PLLA fibers preferably used for the stent fabrication can be loaded with a non-steroid type anti-inflammation agent, such as curcumin. The curcumin-loaded fibers significantly reduce inflammation at the stent implant site by reducing the adhesion of inflammatory cells. Other drugs can be used with the expandable biodegradable polymer stent of the present invention. The impregnated drugs can be prepared in a way that controllably delivers the drug over a predetermined time period.

FIGS. 3A and 3B show an alternate embodiment of the inventive stent, generally designated by reference numeral 100. The stent 100 has a furled state shown in FIG. 3A in which the fiber coils are tightly furled and central lobes 120 (one shown) are confined to a small diameter. There are three peripheral lobes per coil, which are designated by numerals 130 and, in this embodiment, are located inside the central lobes 120. As in the previously-described embodiment of the stent 10 shown in FIG. 1, there may be twelve coils, which are formed from a continuous cord and extend longitudinally to define the body of the stent 100. Each coil has a large central lobe 120 and three internally-disposed peripheral lobes 130, shown in FIG. 3A. As in the previously described stent 10, the stent 100 has longitudinally extending rods 140 that support the coil structure. When the stent 100 is expanded as shown in FIG. 3B, the peripheral lobes merge into a single large-diameter central lobe 120 for each of the twelve coils of the stent 100. Using this construction of internal peripheral lobes 130, the ratio of the final expanded stent diameter to the initial furled stent diameter can be greater than a factor of two.

Those skilled in the art will appreciate that the inventive stent, in its disclosed embodiments or variations thereof, provides mechanical and therapeutic advantages over conventional stents. In addition, advantageous treatments will suggest themselves to the skilled practitioner considering the foregoing description of the invention. By virtue of the biodegradable polymeric nature of the inventive stent, the same vessel site can be retreated at a later time if needed, including staging procedures during growth of the patient. Similarly, successive treatments of a tissue that is changing size can be facilitated with the disclosed stent. It should-also be noted that the inventive stent can be implanted at a site of healthy tissue for diagnostic purposes or therapeutic treatment of adjacent tissue.

Although preferred embodiments have been described and illustrated, it should be understood that various changes, substitutions and alterations can be made therein without departing from the spirit and scope of the invention as defined by the appended claims. 

1-20. (canceled)
 21. An implantable vascular stent having a compressed configuration and an expanded configuration, comprising: at least one fiber cord defining a repeating structure orbiting and extending along a central axis of the stent, the repeating structure having a plurality of furled segments formed of a first length of the fiber cord and each connecting the proximal ends of two adjacent cord segments, each cord segment formed of a second length of the fiber cord; wherein in the compressed configuration, the total length between the distal ends of the two adjacent cord segments is less than the sum of the first length and twice of the second length; wherein the repeating structure is adapted to inelasticly expand into a substantially helical shape about the central axis in the expanded configuration such that the total length between the distal ends of the two adjacent cord segments is approximately equal to the sum of the first length and twice of the second length.
 22. The implantable vascular stent of claim 21 wherein the repeating structure is adapted to expand into a substantially helical shape, in part, by the unfurling of the furled segments.
 23. The implantable vascular stent of claim 22 wherein the fiber cord has an elastic limit such that actuation stress forces exceeding the elastic limit will set the repeating structure in the substantially helical shape following removal of an expanding stress forces.
 24. The implantable vascular stent of claim 21 wherein the repeating structure is adapted to expand into a substantially helical shape, in part, by the deformation of the cord segments.
 25. The implantable vascular stent of claim 21 wherein the repeating structure is adapted to be expanded by a removably insertable inflatable membrane.
 26. The implantable vascular stent of claim 21 wherein the repeating structure is adapted to be expanded by the body heat of a host.
 27. The implantable vascular stent of claim 21, further comprising a series of longitudinal rods extending along the repeating structure parallel to the central axis and attached to one or more of the cord segments.
 28. The implantable vascular stent of claim 21 wherein the furled segments extend inward from the repeating structure toward the central axis of the stent.
 29. The implantable vascular stent of claim 21 wherein the furled segments extend outward away from the central axis of the stent
 30. The implantable vascular stent of claim 21 wherein the fiber cord is biodegradable within a host.
 31. The implantable vascular stent of claim 21 wherein the fiber cord is adapted to provide medication to an implant site of the stent.
 32. The implantable vascular stent of claim 21 wherein the fiber cord comprises a polymer fiber.
 33. An implantable vascular stent having a compressed configuration and an expanded configuration, comprising: at least one fiber cord defining a repeating structure orbiting and extending along a central axis of the stent, the repeating structure having a plurality of furled segments formed of a first length of the fiber cord and each connecting the proximal ends of two adjacent cord segments, cord segment formed of a second length of the fiber cord; wherein in the compressed configuration, the total length between the distal ends of the two adjacent cord segments is less than the sum of the first length and twice of the second length; wherein the repeating structure is adapted to be substantially irreversibly expanded into a substantially helical shape about the central axis in the expanded configuration such that the total length between the distal ends of the two adjacent cord segments is approximately equal to the sum of the first length and twice of the second length.
 34. An implantable vascular stent having a compressed configuration and an expanded configuration, comprising: at least one fiber cord defining a repeating structure orbiting and extending along a central axis of the stent, the repeating structure having at least one furled segment formed of a first of the fiber cord and connecting the proximal ends of two adjacent cord segments, each cord segment formed of a second length of the fiber cord; wherein in the compressed configuration, the total length between the distal ends of the two adjacent cord segments is less than the sum of the first length and twice of the second length; wherein the repeating structure is adapted to inelasticly expand into a substantially helical shape about the central axis in the expanded configuration such that the total length between the distal ends of the two adjacent cord segments is approximately to the sum of the first length and twice of the second length. 